?鹽水浸泡試驗箱EN ISO 8442、GB標準而制造的專用檢測設備
EN ISO 8442-2:1998標準中關于鹽水浸泡測試的內容如下：
C.4.2 Fill the container with the sodium chloridesolution (see C.2) using at least 1 litre of solution for every square decimetre of area of the stainless steel parts of the samples. Bring the container and contents to 60 °C ± 2 °C. Maintain at this temperature. Do not allow the temperature of the solution to exceed 62 °C at any time, even before the start of the test. Use a fresh sodium chloride solution for each test.
NOTE The temperature of the sodium chloride solution may be conveniently maintained at 60 °C ± 2 °C by positioning the apparatus in a thermostatically controlled water bath, the level of which is maintained at approximately the same level as that of the sodium chloride solution.
C.4.3 Place the test specimen in the rack and, in the case of knives with stainless steel handles, support the handles in such a way that they do not come into contact with the rack. Replace the cover.
C.4.4 Completely immerse and completely withdraw the test specimens from the solution at the rate of from two to three times per minute for 6 h.
C.4.5 At the conclusion of the test period, thoroughly wash and rinse the test specimens and examine for corrosion.
NOTE Products of corrosion that impede visual examination of corrosion pits should be removed by hａnd rubbing the surface of the cutlery with a stainless steel polishing paste applied with asoft cloth.
C.5 Expression of results Assess the size and number of pits per test specimen and the length of longitudinal cracks visually with the aid of a calibrated microscope or lens of at least four times magnification. Where two pits have obviously merged together they shall be assessed as
two separate pits.
NOTE The use of wires of diameter 0,4 mm and 0,75 mm respectively, placed in contact with the sample surface, provides a convenient method of assessing the size of pits with a hａnd lens.
針對上述ISO 8442-2:1998測試標準要求，科迪儀器專業生產封閉式鹽水噴霧試驗箱和開放式鹽水浸泡試驗箱，保證測試產品浸入在鹽水中和停留在空氣中每分鐘2到3次，連續進行6個小時的測試。
鹽水浸泡試驗箱技術要點：
1、鹽水溫度：RT+5到60度范圍內可設定；
2、根據特定產品可制作不同的夾具；
3、升降裝置做到每分鐘升降2到4次可調；
4、加熱器不以金屬材質接觸鹽水。
5、內箱尺寸可根據客戶產品大小而定做。
?